T2 copper plate, copper stick, copper tube, copper row, copper row, copper belt, H65 brass plate

T2 copper plate, copper stick, copper tube, copper row, copper row, copper belt, H65 brass plate

Material name: T2 Copper Band Chemical Composition: Silver+ Copper+ Silver CUAG: ≥99.9 Nickel Ni Ni: ≤0.005 Iron FE: ≤ 0.005 铍 SB: ≤0.002 Sulfur s: ≤0.002 ≤ ≤: ≤0.001: oxygen O: ≤0.06 (impurities) Note: ≤0.1 Mechanical performance: tensile strength σb (MPA): ≥205 elongation rate Δ10 ( %): ≥30 % Note: ≥0.3 Sample size: thickness and heat treatment specification: Thermal processing temperature 900 ~ 1050 ℃ annealing temperature of 500 ～ 700 ℃ Copper series Copper series, named after purple -red. It is not necessarily pure copper. Sometimes it also adds a small amount of deoxysentery or other elements to improve the material and performance, so it is also attributed to copper alloy. High purity, fine tissue, and extremely low oxygen content. Pores, trachoma, loose, conductive performance, high surface accuracy of the molds from electrostatic erosion, processing process through heat treatment, the electrode has no directionality, suitable for fine -bearing, detailed, and good thermal power channels, processabil

材质名称:T2紫铜带

化学成分：

银 + 铜+银 CuAg:≥99.9

镍 Ni:≤0.005

铁 Fe:≤0.005

铍 Sb :≤0.002

硫 S :≤0.005

砷 As :≤0.002

铋 Bi:≤0.001 :

氧 O:≤0.06 （ 杂质) 注:≤0.1

力学性能:

抗拉强度 σb (MPa):≥205 

 伸长率 δ10 (%):≥30 %

注 :带材的室温拉伸力学性能 

试样尺寸:厚度≥0.3 

试样尺寸:厚度 

热处理规范:

热加工温度 900～1050℃

退火温度 500～700℃

紫铜带系列紫铜，因呈紫红色而得名。它不一定是纯铜，有时还加入少量脱氧元素或其他元素,以改善材质和性能,因此也归入铜合金。

用途

高纯度，组织细密，含氧量极低。无气孔、沙眼、疏松，导电性能，电蚀出的模具表面精度高，经热处理工艺，电极无方向性，适合精打，细打，具有良好的热电道性、加工性、延展性、防蚀性及耐候性等。有良好的导电、导热、耐蚀和加工性能,可以焊接和钎焊。